Item Unit Test Method Special
H140-54C
High Strength, Fuel Resistant
Color No. CF2001
ISO Marking Code ISO11469
(JIS K6999)
>POM<
Density g/cm³ ISO 1183 1.42
Water absorption (23°C,24hrs,1mmt) % ISO 62 0.5
MFR (190℃、2.16kg) g/10min ISO 1133 14
MVR (190℃, 2.16kg) cm³/10min ISO 1133 12
Tensile strength MPa ISO 527-1,2 71
Strain at break % ISO 527-1,2 30 *1
Tensile modulus MPa ISO 527-1,2 2,900
Flexural strength MPa ISO 178 95
Flexural modulus MPa ISO 178 2,800
Charpy notched impact strength (23℃) kJ/m² ISO 179/1eA 6.0
Temperature of deflection under load (1.8MPa) ISO 75-1,2 100
Coefficient of linear thermal expansion (23 - 55℃、Flow direction) x10-5/℃ Our standard 10
Coefficient of linear thermal expansion (23 - 55℃、Transverse direction) x10-5/℃ Our standard 10
Electric strength (3mmt) kV/mm IEC 60243-1 21
Volume resistivity Ω·cm IEC 60093 1 x 1015
Surface resistivity Ω IEC 60093 7 x 1015
Volume resistivity (Our standard) Ω·cm -
Surface resistivity (Our standard) Ω -
Mold Shrinkage (60×60×2mmt, Flow direction, Cavity Pressure 60 MPa) % ISO 294-4 2.2
Mold Shrinkage (60×60×2mmt, Transverse direction, Cavity Pressure 60 MPa) % ISO 294-4 2.3
Rockwell hardness M(Scale) ISO2039-2 94
Specific wear amount (Thrust, vs C-Steel, material side, pressure 0.49MPa, 30cm/s) x10-3mm³/(N·km) JIS K7218 1.23
Specific wear amount (Thrust, vs C-Steel, steel side, pressure 0.49MPa, 30cm/s) x10-3mm³/(N·km) JIS K7218 < 0.01
Coefficient of Dynamic Friction (Thrust, vs C-Steel, pressure 0.49MPa, 30cm/s) JIS K7218 0.48
Specific wear amount (Thrust, vs C-Steel, material side, pressure 0.98MPa, 30cm/s) x10-3mm³/(N·km) JIS K7218 0.83
Specific wear amount (Thrust, vs C-Steel, steel side, pressure 0.98MPa, 30cm/s) x10-3mm³/(N·km) JIS K7218 < 0.01
Coefficient of Dynamic Friction (Thrust, vs C-Steel, pressure 0.98MPa, 30cm/s) JIS K7218 0.38
Specific wear amount (Thrust, vs M90-44, material side, pressure 0.06MPa, 15cm/s) x10-3mm³/(N·km) JIS K7218 80.9
Specific wear amount (Thrust, vs M90-44, M90-44 side, pressure 0.06MPa, 15cm/s) x10-3mm³/(N·km) JIS K7218 56.8
Coefficient of Dynamic Friction (Thrust, vs M90-44, pressure0.06MPa, 15cm/s) JIS K7218 0.37
Flammability   UL94 -
The yellow card File No.     -
Appropriate List number of Ministerial Ordinance for Export Trade Control     Item 16 of Appendix -1

If item's description doesn't include test condition, the item is examined at 23 deg. C. (RT)
Details of each property item, test conditions, please see here

*1) Nominal strain at break

All figures in the table are the typical values of the material and not the minimum values of the material specifications.
All data shown here are not always applicable to parts used under different conditions. We do not guarantee that these data are directly applicable to the application conditions of users and we ask each user to make his own decision on the application.
For safe handling of materials we supply, it is advised to refer to the Material Safety Data Sheet “SDS” of the proper material.
This brochure is edited based on reference literatures, information and data currently available to us. So the contents of this brochure are subject to change without notice due to new data.