| 項目 | 単位 | 試験方法 | Glass Fiber Reinforced | |
| GH-20 | ||||
| GF20% Reinforced | ||||
| カラー | CF3500 | |||
| ISO(JIS)材質表示 | ISO11469 (JIS K6999) |
>POM-GF20< | ||
| Density | g/cm³ | ISO 1183 | 1.54 | |
| Water absorption (23°C,24hrs,1mmt) | % | ISO 62 | 0.7 | |
| MFR (190℃, 2160g) | g/10min | ISO 1133 | 3.0 | |
| MVR (190℃, 2.16kg) | cm³/10min | ISO 1133 | 2.3 | |
| Tensile strength | MPa | ISO 527-1,2 | 100 | |
| Strain at break | % | ISO 527-1,2 | 2.0 | |
| Tensile modulus | MPa | ISO 527-1,2 | 7,000 | |
| Flexural strength | MPa | ISO 178 | 135 | |
| Flexural modulus | MPa | ISO 178 | 6,000 | |
| Charpy notched impact strength (23℃) | kJ/m² | ISO 179/1eA | 5.2 | |
| Temperature of deflection under load (1.8MPa) | ℃ | ISO 75-1,2 | 158 | |
| Coefficient of linear thermal expansion (23 - 55℃、Flow direction) | x10-5/℃ | Our standard | 3 | |
| Coefficient of linear thermal expansion (23 - 55℃、Transverse direction) | x10-5/℃ | Our standard | 10 | |
| Electric strength (3mmt) | kV/mm | IEC 60243-1 | - | |
| Volume resistivity | Ω·cm | IEC 60093 | - | |
| Surface resistivity | Ω | IEC 60093 | - | |
| Volume resistivity (Our standard) | Ω·cm | - | ||
| Surface resistivity (Our standard) | Ω | - | ||
| Mold Shrinkage (60×60×2mmt, Flow direction, Cavity Pressure 60 MPa) | % | ISO 294-4 | 0.8 | |
| Mold Shrinkage (60×60×2mmt, Transverse direction, Cavity Pressure 60 MPa) | % | ISO 294-4 | 1.1 | |
| Rockwell hardness | M(Scale) | ISO2039-2 | 85 | |
| Specific wear amount (Thrust, vs C-Steel, material side, pressure 0.49MPa, 30cm/s) | x10-3mm³/(N·km) | JIS K7218 | 70 | |
| Specific wear amount (Thrust, vs C-Steel, steel side, pressure 0.49MPa, 30cm/s) | x10-3mm³/(N·km) | JIS K7218 | 2.0 | |
| Coefficient of Dynamic Friction (Thrust, vs C-Steel, pressure 0.49MPa, 30cm/s) | JIS K7218 | 0.55 | ||
| Specific wear amount (Thrust, vs C-Steel, material side, pressure 0.98MPa, 30cm/s) | x10-3mm³/(N·km) | JIS K7218 | - | |
| Specific wear amount (Thrust, vs C-Steel, steel side, pressure 0.98MPa, 30cm/s) | x10-3mm³/(N·km) | JIS K7218 | - | |
| Coefficient of Dynamic Friction (Thrust, vs C-Steel, pressure 0.98MPa, 30cm/s) | JIS K7218 | - | ||
| Specific wear amount (Thrust, vs M90-44, material side, pressure 0.06MPa, 15cm/s) | x10-3mm³/(N·km) | JIS K7218 | 3.0 | |
| Specific wear amount (Thrust, vs M90-44, M90-44 side, pressure 0.06MPa, 15cm/s) | x10-3mm³/(N·km) | JIS K7218 | 100 | |
| Coefficient of Dynamic Friction (Thrust, vs M90-44, pressure0.06MPa, 15cm/s) | JIS K7218 | 0.42 | ||
| 燃焼性 | UL94 | HB | ||
| UL イエローカード File No. | E45034 *2 | |||
| 「輸出貿易管理令」の該当項番 | Item 16 of Appendix -1 | |||
試験条件について特に記載のないものは、常温(23℃)で測定されたデータとなります。
各物性項目の、試験条件の詳細はこちらをご参照ください
*2) イエローカード記載のデータは、色や肉厚等の条件によって限定されているものもありますので、内容をよくご確認の上でご使用ください。
詳細物性データ
| Moldability | Mold Shrinkage | データを表示する |
上記の値は材料の射出成形時における代表的な測定値であり、材料規格に対する最低値ではありません。ここに示したデータは異なった条件下で使用される部品にそのまま適用できるとは限りません。