9506F-500 (ISO)

PRINT
No Word
Counterfeit Products Alert
Item Unit Test Method Film
9506F-500
Improved Moldability, Low Tg
Color No. -
ISO Marking Code ISO11469
(JIS K6999)
>COC<
Density kg/m³ ISO 1183 1,010
Water absorption (23°C, sat.) % ISO 62 0.01
MVR (190℃, 2.16kg) cm³/10min ISO 1133 1.0
MVR (230℃, 2.16kg) cm³/10min ISO 1133 6.0
Glass transition temperature (10℃/min) ISO 11357-1,-2,-3 65
Tensile modulus (Film) (machine direction) MPa ISO 527-3 1,800
Tensile modulus (Film) (transverse direction) MPa ISO 527-3 1,700
Tensile strength at break (Film) (machine direction) MPa ISO 527-3 52
Tensile strength at break (Film) (transverse direction) MPa ISO 527-3 51
Elongation at break (Film) (machine direction) % ISO 527-3 3.1
Elongation at break (Film) (transverse direction) % ISO 527-3 3.1
Water vapor permeability (Film) (38℃, 90%RH) g・100μm/(m²・day) ISO 15106-3 0.90
Flammability   UL94 -
The yellow card File No.     -
Appropriate List number of Ministerial Ordinance for Export Trade Control     -

If item's description doesn't include test condition, the item is examined at 23 deg. C. (RT)
Details of each property item, test conditions, please see here

All figures in the table are the typical values of the material and not the minimum values of the material specifications.
All data shown here are not always applicable to parts used under different conditions. We do not guarantee that these data are directly applicable to the application conditions of users and we ask each user to make his own decision on the application.
For safe handling of materials we supply, it is advised to refer to the Material Safety Data Sheet “SDS” of the proper material.
This brochure is edited based on reference literatures, information and data currently available to us. So the contents of this brochure are subject to change without notice due to new data.