Item Unit Test Method Low VOC Low VOC Low VOC
M90LV NW-02LV TF-10LV
Standard High Sliding Tough
Color No. CF2001/CD3069 CF2001/CD3501 CF2003 / CF2004
ISO Marking Code ISO11469
(JIS K6999)
>POM< >POM+PE< >POM-I<
Density g/cm³ ISO 1183 1.41 1.36 1.38
Water absorption (23°C,24hrs,1mmt) % ISO 62 0.6 0.7 0.7
MFR (190℃、2.16kg) g/10min ISO 1133 9 20 10
MVR (190℃, 2.16kg) cm³/10min ISO 1133 8 18 9
Tensile strength MPa ISO 527-1,2 60 52 46
Strain at break % ISO 527-1,2 35 *1 20 *1 55 *1
Tensile modulus MPa ISO 527-1,2 2,640 2,250 1,850
Flexural strength MPa ISO 178 83 68 60
Flexural modulus MPa ISO 178 2,350 2,100 1,700
Charpy notched impact strength (23℃) kJ/m² ISO 179/1eA 7.0 5.9 12
Temperature of deflection under load (1.8MPa) ISO 75-1,2 93 80 82
Coefficient of linear thermal expansion (23 - 55℃、Flow direction) x10-5/℃ Our standard 12 12 13
Coefficient of linear thermal expansion (23 - 55℃、Transverse direction) x10-5/℃ Our standard 12 12 13
Electric strength (3mmt) kV/mm IEC 60243-1 - - -
Volume resistivity Ω·cm IEC 60093 3 x 1014 - 1 x 1013
Surface resistivity Ω IEC 60093 3 x 1016 - 7 x 1012
Volume resistivity (Our standard) Ω·cm - - -
Surface resistivity (Our standard) Ω - - -
Mold Shrinkage (60×60×2mmt, Flow direction, Cavity Pressure 60 MPa) % ISO 294-4 2.4 2.4 2.1
Mold Shrinkage (60×60×2mmt, Transverse direction, Cavity Pressure 60 MPa) % ISO 294-4 2.3 2.2 2.0
Rockwell hardness M(Scale) ISO2039-2 80 - 65
Specific wear amount (Thrust, vs C-Steel, material side, pressure 0.49MPa, 30cm/s) x10-3mm³/(N·km) JIS K7218 1.5 - 1.0
Specific wear amount (Thrust, vs C-Steel, steel side, pressure 0.49MPa, 30cm/s) x10-3mm³/(N·km) JIS K7218 < 0.01 - < 0.01
Coefficient of Dynamic Friction (Thrust, vs C-Steel, pressure 0.49MPa, 30cm/s) JIS K7218 0.47 - 0.30
Specific wear amount (Thrust, vs C-Steel, material side, pressure 0.98MPa, 30cm/s) x10-3mm³/(N·km) JIS K7218 - 0.19 -
Specific wear amount (Thrust, vs C-Steel, steel side, pressure 0.98MPa, 30cm/s) x10-3mm³/(N·km) JIS K7218 - < 0.01 -
Coefficient of Dynamic Friction (Thrust, vs C-Steel, pressure 0.98MPa, 30cm/s) JIS K7218 - 0.17 -
Specific wear amount (Thrust, vs M90-44, material side, pressure 0.06MPa, 15cm/s) x10-3mm³/(N·km) JIS K7218 - 4.0 7.0
Specific wear amount (Thrust, vs M90-44, M90-44 side, pressure 0.06MPa, 15cm/s) x10-3mm³/(N·km) JIS K7218 - 10 6.0
Coefficient of Dynamic Friction (Thrust, vs M90-44, pressure0.06MPa, 15cm/s) JIS K7218 0.37 0.32 0.60
Flammability   UL94 HB HB -
The yellow card File No.     E45034 *2 E45034 *2 -
Appropriate List number of Ministerial Ordinance for Export Trade Control     Item 16 of Appendix -1 Item 16 of Appendix -1 Item 16 of Appendix -1

If item's description doesn't include test condition, the item is examined at 23 deg. C. (RT)
Details of each property item, test conditions, please see here

*1) Nominal strain at break
*2) Some of the data described on Yellow Card are limited to specific conditions (color, thickness etc.). Please carefully view the detailed descriptions on the Card.

Data of detailed properties

    M90LV NW-02LV TF-10LV
Moldability  Mold Shrinkage  To view the data   To view the data    
Short-term mechanical properties  Flexural Properties  To view the data      
Short-term mechanical properties  Effect of Temperature on Maximum Stress  To view the data      
Short-term mechanical properties  Effect of Temperature on Modulus  To view the data      

All figures in the table are the typical values of the material and not the minimum values of the material specifications.
All data shown here are not always applicable to parts used under different conditions. We do not guarantee that these data are directly applicable to the application conditions of users and we ask each user to make his own decision on the application.
For safe handling of materials we supply, it is advised to refer to the Material Safety Data Sheet “SDS” of the proper material.
This brochure is edited based on reference literatures, information and data currently available to us. So the contents of this brochure are subject to change without notice due to new data.