HOME   >  Product Introduction  >  Product Lines  >  TOPAS(COC)  > 
  Properties

Top Raw material/Polymerization Characteristics Properties Applications
   
Property of TOPAS® grades (361KB)
Unit Test Method Grades
8007 6013 6015 5013 6017
Property
 Volume flow index MVR
(260°C/2.16kg) 		ml/10min ISO 1133 32 14 4 48 1.5
Volume flow index MVR
(HDT/B+115°C/2.16kg)		 ml/10min ISO 1133 2 6 5 25 5
Density g/cm3 ISO 1183 1.02 1.02 1.02 1.02 1.02
Water absorption,immersion @23°C % ISO 62 0.01 0.01 0.01 0.01 0.01
Water permeability @23°C 85RH% g·mm/m2·d DIN 53 122 0.023 0.035 0.035 0.030 0.045
Mechanical Property
 Tensile modulus (1mm/min) MPa ISO 527
parts 1 and 2		 2600 2900 3000 3200 3000
Tensile strength at break (5mm/min) MPa 63* 63 60 46 58
Tensile elongation at break (5mm/min) % 4.5* 2.7 2.5 1.7 2.4
Charpy impact strength (unnotched) KJ/m2 ISO 179/1eU 20 15 15 13 15
Charpy impact strength (notched) KJ/m2 ISO 179/1eA 2.6 1.8 1.6 1.6 1.6
Pencil hardness - JIS K5401 HB HB HB F F
Thermal Property
 Glass transition temperature °C ISO 11375-2 80 140 160 136 180
Heat deflection temperature at 0.45MPa °C ISO 75
parts 1 and 2		 75 130 150 127 170
Heat deflection temperature at 1.80MPa °C 68 119 135 116 151
Optical Property
 Light transmittance % ISO 13468-1 91 91 91 91 91
Refractive index - ISO 489 1.53 1.53 1.53 1.53 1.53
Abbe number - - - - - 58 -
* test speed 50mm/min
** As the values above have not been fully verified statistically, they may be subject to change.
    Do not use them for specifications.